| About |
|---|
| High performance thermoplastic material, unreinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, depth filtered granules for injection moulding, standard flow, colour natural/beige. Applications for high strength and stiffness as well as good ductility at higher temperatures. Chemically resistant to aggressive environments.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Ductility,High Heat Resistance,Hypocrystalline,Good Rigidity |
| Availabilitys | Africa & Middle East ,Asia Pacific,Latin America,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179 | |
| Izod Notched Impact strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 180-A |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 172 | ℃ | ISO 75-2/Af |
| Glass Transition Temperature | |||
| — | 162 | ℃ | |
| — | 169 | ℃ | |
| Melting temperature | 387 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | |||
| MD：< 162℃ | 4.5E-5 | 1/℃ | |
| MD：> 162℃ | 1.1E-4 | 1/℃ | |
| TD：< 162℃ | 5.5E-5 | 1/℃ | |
| TD：> 162℃ | 1.3E-4 | 1/℃ | |
| Thermal conductivity | |||
| 23℃ | 0.29 | W/m/K | |
| 23℃ | 0.32 | W/m/K |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | |||
| 23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 2.5 mm | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23 ℃，1 kHz | 3.00 | IEC 60250 | |
| Dissipation Factor | |||
| 23℃，1 MHz | 4.0E-3 | IEC 60250 | |
| Compared Tracking Index | 150 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 85 | ISO 868 | |
| Tensile Modulus | |||
| 23℃ | 4200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield yld, 23 ℃ | 115 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 25 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23℃ | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23℃ | 190 | MPa | |
| 3.50% strain, 23 ℃ | 130 | MPa | |
| 125℃ | 110 | MPa | |
| 175℃ | 35.0 | MPa | |
| 275℃ | 20.0 | MPa | |
| Compressive Strength | |||
| 23℃ | 145 | MPa | |
| 120℃ | 90.0 | MPa | |
| 200℃ | 35.0 | MPa |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Spiral flow length | |||
| — | 16.0 | cm | |
| — | 19.0 | cm | |
| — | 68.0 | cm | |
| Molding shrinkage | |||
| TD | 1.6 | % | |
| TD | 1.2 | % | |
| MD | 1.4 | % | |
| MD | 1.1 | % | |
| Water Absorption | |||
| Saturation, 100 ℃ | 0.95 | % | ISO 62 |
| Apparent viscosity | |||
| 420℃ | 225 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 150 to 180 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature Zone 1 | 375 | °C | |
| Middle Temperature Zone 2 | 380 to 385 | °C | |
| Front Temperature Zone 3 | 390 | °C | |
| Nozzle temperature | 395 | °C | |
| Mold Temperature | 200 to 220 | °C | |
| Mold Temperature – Maximum | 250 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Crystalline |
| 3. Mold Temperature: 392°F, Melt Temperature: 743°F |
| 4. 1 mm |
| 5. Mold Temperature: 428°F, Melt Temperature: 779°F |
| 6. 3 mm |
| 7. 395°C nozzle, 200°C tool |
| 8. 415°C nozzle, 220°C tool |
| 9. at Yield |
| 10. Onset |
| 11. Midpoint |
| 12. Average |
| 13. Along flow |
| 14. Result based on 450G |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |