| About |
|---|
| High performance thermoplastic material, unreinforced PolyEtherKetoneEtherKetoneKetone (PEKEKK), semi crystalline, coarse powder for extrusion compounding, low flow, colour natural.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Hypocrystalline,Low liquidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Modulus | |||
| 23℃ | 4200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield yld, 23 ℃ | 110 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Broken BRK, 23 ℃ | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23℃ | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23℃ | 170 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-A |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-2 | ||
| — | 162 | ℃ | ISO 11357-2 |
| — | 169 | ℃ | ISO 11357-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Apparent viscosity | |||
| 420℃ | 225 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 150 to 180 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Melt Temperature | 410 to 420 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Crystalline |
| 3. Onset |
| 4. Midpoint |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |