| F010-H2O-00 Coating System for Potable Water POTABLE WATER NSF/ANSI 61 Certified Vipel F010-H2O-00 is certified to NSF/ANSI 61 for use in commercial and domestic potable water systems as a protective barrier material. If fabricators follow the ingredients and process instructions listed on page 3, they do not need to perform additional testing to manufacture a NSF/ANSI 61 compliant coating. BENEFITS Suitable for Sodium Hypochlorite Containment The formulation of Vipel F010-H2O-00 is also appropriate and suitable for sodium hypochlorite (chlorine bleach) containment. Sodium hypochlorite is a widely accepted water purification chemical that is very aggressive to most metals and many polymeric materials. The use of coatings that are not formulated for sodium hypochlorite containment will reduced the service life of the equipment.&& |
| Product Description | |
|---|---|
| Generic | 乙烯基酯 |
| Material Status | Commercial: Active |
| Features | Alkali resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| styrene content | 39 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ASTM D648 |
| Glass transition temperature | 130 | ℃ | DIN 53445 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | ohms | DIN 53482 |
| Volume resistivity | > 1.0E+16 | ohms·cm | DIN 53482 |
| Dielectric strength | |||
| 0.7 mm | 120 | kV/mm | DIN 53481 |
| Dielectric constant | DIN 53483 | ||
| 60 Hz | 3.40 | DIN 53483 | |
| 60 Hz | 3.50 | DIN 53483 | |
| 1 kHz | 3.40 | DIN 53483 | |
| 1 kHz | 3.50 | DIN 53483 | |
| 1 MHz | 3.30 | DIN 53483 | |
| 1 MHz | 3.40 | DIN 53483 | |
| Dissipation factor | DIN 53483 | ||
| 60 Hz | 2.5E-3 | DIN 53483 | |
| 60 Hz | 3.7E-3 | DIN 53483 | |
| 1 kHz | 2.2E-3 | DIN 53483 | |
| 1 kHz | 3.3E-3 | DIN 53483 | |
| 1 MHz | 1.6E-3 | DIN 53483 | |
| 1 MHz | 2.3E-3 | DIN 53483 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Critical Strain Energy | 100 | J/m² | ASTM E399 |
| Gel to Peak | 10.0 | min | |
| exothermic peak | 180 | ℃ | |
| Stress Intensity Factor | 0.600 | ASTM E399 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | |
| viscosity | |||
| 25℃，Brookfield RVT | 0.30 | Pa·s | |
| Gelation time | |||
| 25℃ | 20 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Babbitt hardness | 39 | ASTM D2583 | |
| Tensile modulus | 3170 | MPa | ASTM D638 |
| tensile strength | 88.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.2 | % | ASTM D638 |
| Bending modulus | 3450 | MPa | ASTM D790 |
| bending strength | 152 | MPa | ASTM D790 |
| compressive strength | 121 | MPa | ASTM D695 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. after 24 hrs in drinking water |
| 3. Dry |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |