Vipel® F085-AAA-00

About
The Vipel F085 series is an epoxy novolac vinyl ester resin dissolved in styrene. 085 series is ideally suited for applications where outstanding mechanical properties and resistance to chemicals, oxidation and heat are required. BENEFITS Corrosion Resistance The epoxy novolac backbone chemistry provides resistance to acids and bases and has superior resistance to many organic solvents. The F085 series is generally resistant to liquids and vapors at higher temperatures than standard bisphenol-A epoxy vinyl ester resins. The F085 series is well suited for use in the field of chlorine-alkali electrolysis. Refer to AOC’s “Corrosion Resistant Resin Guide” for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment, contact AOC. Mechanical Properties The F085 series is suitable for moldings that are subjected to particularly high static and dynamic loads. It is resistant to internal stress cracking under high loading. Versatile Suitable for various fabricating methods such as hand lay-up, filament winding, etc.&&

About

The Vipel F085 series is an epoxy novolac vinyl ester resin dissolved in styrene. 085 series is ideally suited for applications where outstanding mechanical properties and resistance to chemicals, oxidation and heat are required. BENEFITS Corrosion Resistance The epoxy novolac backbone chemistry provides resistance to acids and bases and has superior resistance to many organic solvents. The F085 series is generally resistant to liquids and vapors at higher temperatures than standard bisphenol-A epoxy vinyl ester resins. The F085 series is well suited for use in the field of chlorine-alkali electrolysis. Refer to AOC’s “Corrosion Resistant Resin Guide” for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment, contact AOC. Mechanical Properties The F085 series is suitable for moldings that are subjected to particularly high static and dynamic loads. It is resistant to internal stress cracking under high loading. Versatile Suitable for various fabricating methods such as hand lay-up, filament winding, etc.&&

Product Description
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Alkali resistant,Corrosion Resistant,Acidproof,High Heat Resistance,Inoxidizability,Solvent resistance,High ESCR
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
styrene content	33	%

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	149	℃	ASTM D648

Supplementary information	Nominal value	Unit	Test method
Gel to Peak	5.0	min
exothermic peak	204	℃

Uncured Properties	Nominal value	Unit
Density	1.08	g/cm³
viscosity
25℃，Brookfield RVT	0.30	Pa·s
Gelation time
25℃	15	min

MECHANICAL	Nominal value	Unit	Test method
Babbitt hardness	44		ASTM D2583
Tensile modulus	3720	MPa	ASTM D638
tensile strength	77.2	MPa	ASTM D638
Tensile strain
fracture	3.3	%	ASTM D638
Bending modulus	3720	MPa	ASTM D790
bending strength	148	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.