| About |
|---|
| Vistamaxx 3020FL is primarily composed of isotactic propylene repeat units with random ethylene distribution. It is produced using ExxonMobil’s proprietary metallocene catalyst technology. The ‘FL’ designates this product passes ExxonMobil’s test for film appearance with regard to gels, as needed for performance film applications (‘A’ rating).&& |
| Product Description | |
|---|---|
| Supplier | ExxonMobil |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.874 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.1 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 34 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| fracture | 17.0 | MPa | ASTM D638 |
| yield | 4.65 | MPa | ASTM D638 |
| 100% strain | 4.39 | MPa | ASTM D638 |
| 300% strain | 4.40 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1800 | % | ASTM D638 |
| yield | 47 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 59.7 | MPa | ASTM D790 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 64.3 | kN/m | ASTM D624 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Property specified in conventional unit of measure. |
| 3. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |