| VITAMIDE® BF13BL6262是一种聚酰胺6（尼龙6）产品,。 它,在欧洲有供货。 特性包括: 阻燃/额定火焰 Flame Retardant&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 , ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 1.0 | % | ASTM D570，ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 70.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 25 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2750 | MPa | ASTM D790 , ISO 178 |
| bending strength | 90.0 | MPa | ASTM D790，ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 5.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed | 100 | ℃ | ASTM D648，ISO 75-2/A |
| Melting temperature | 220 | ℃ | ISO 1218，ASTM D2117 |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257，IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| CTI | 600 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |