| VITAMIDE® TS20RD6369是一种聚酰胺66/6共聚物（尼龙66/6）产品,。 它,在欧洲有供货。 特性包括: 阻燃/额定火焰 紫外线稳定&& |
| Product Description | |
|---|---|
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Low to no calcium content,HB |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 , ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 1.3 | % | ASTM D570，ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 80.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | 30 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 2400 | MPa | ASTM D790 , ISO 178 |
| bending strength | |||
| — | 95.0 | MPa | ISO 178 |
| fracture | 95.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | 5.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 205 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa, unannealed | 90.0 | ℃ | ASTM D648，ISO 75-2/A |
| Melting peak temperature | 240 | ℃ | ASTM D2117 , ISO 1218 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257，IEC 60093 |
| Dielectric strength | 26 | kV/mm | ASTM D149，IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 | |
| Extreme oxygen index | 24 | % | ASTM D2863，ISO 4589-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |