| About |
|---|
| Viton® B-600 fluoroelastomer is a gum polymer that demonstrates improved terpolymer processing and lower compound viscosity, along with the excellent heat and fluid resistance characteristics of the “B-family” of Viton®. Viton® B-600 is especially suited to curing with the bisphenol system: Viton® Curative No. 20 and No. 30 or Viton® Curative No. 50. Compared to Viton® B, Viton® B-600 provides: Improved compression molding increased mold flow easier mold release Improved extrusion and calendering Increased cure rate Improved compression set resistance Applications Viton® B-600 is highly recommended for applications like: Molded goods, e.g., shaft seals Calendered goods, e.g., flue duct expansion joints&& |
| Product Description | |
|---|---|
| Supplier | Chemours |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good liquidity |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.85 | g/cm³ | ASTM D792 |
| Mooney viscosity | |||
| ML 1+10，121℃ | 65 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 23 ℃ | 68 | ASTM D2240 | |
| Shore A, 23 ℃ | 74 | ASTM D2240 | |
| Shore A, 23 ℃ | 71 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| 100% strain, 23 ℃ | 3.60 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 6.30 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 3.00 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| Yield, 23 ℃ | 7.70 | MPa | ASTM D412 |
| Yield, 23 ℃ | 13.0 | MPa | ASTM D412 |
| Yield, 23 ℃ | 8.30 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| Fracture, 23 ℃ | 250 | % | ASTM D412 |
| Fracture, 23 ℃ | 220 | % | ASTM D412 |
| Fracture, 23 ℃ | 340 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 200℃，22 hr | 13 | % | ASTM D395B |
| 200℃，70 hr | 22 | % | ASTM D395B |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume change | ASTM D471 | ||
| 23 ℃, 70 hr, C-grade standard fuel | 3.0 | % | ASTM D471 |
| 23 ℃, 70 hr, methanol | 19 | % | ASTM D471 |
| 150℃，70 hr，in Sulfuric Acid 96% | 22 | % | ASTM D471 |
| 175 ℃, 70 hr, in Stauffer 7700 liquid | 9.0 | % | ASTM D471 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 20 in/min, Aged in Sulfuric Acid 96% for 70 hr at 302°F |
| 3. 20 in/min, Aged for 24 hr at 450°F |
| 4. 20 in/min, Aged for 70 hr at 527°F |
| 5. Aged in Sulfuric Acid 96% for 70 hr at 302°F |
| 6. Aged for 24 hr at 450°F |
| 7. Aged for 70 hr at 527°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |