| About |
|---|
| Viton® GFLT-600S fluoroelastomer is a 67% fluorine, peroxide-cured, low temperature fluoroelastomer. GFLT-600S utilizes the latest technology, Advanced Polymer Architecture (APA), which includes a novel peroxide cure site along with an optimized molecular weight distribution. Features Cures exceptionally fast to a high state of cure Similar to improved low temperature properties compared to Viton® GFLT Improved mold release/mold fouling properties Improved mold flow and less shear sensitivity for a 65 Mooney peroxy cured FKM Excellent physical properties with high elongation, both original and aged Heat, fluids, and low temperature resistance comparable to Viton® GFLT Improved water resistance/lower volume swell in water Excellent compression set resistance with either low or no postcure&& |
| Product Description | |
|---|---|
| Supplier | Chemours |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Dimensional Stability,Antifreeze,Good stripping performance,Good Tensile Strength |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.86 | g/cm³ | ASTM D792 |
| Mooney viscosity | |||
| ML 1+10，121℃ | 65 | MU | ASTM D1646 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 23 ℃ | 68 | ASTM D2240 | |
| Shore A, 23 ℃ | 71 | ASTM D2240 | |
| Shore A, 23 ℃ | 70 | ASTM D2240 | |
| Shore A, 23 ℃ | 69 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| 23℃ | 0.700 | MPa | ASTM D412 |
| 23℃ | 0.700 | MPa | ASTM D412 |
| 23℃ | 0.700 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| 10% strain | ASTM D412 | ||
| 100% strain, 23 ℃ | 4.40 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 5.20 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 4.30 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 3.40 | MPa | ASTM D412 |
| tensile strength | ASTM D412 | ||
| Yield, 23 ℃ | 12.2 | MPa | ASTM D412 |
| Yield, 23 ℃ | 8.00 | MPa | ASTM D412 |
| Yield, 23 ℃ | 17.6 | MPa | ASTM D412 |
| Yield, 23 ℃ | 15.0 | MPa | ASTM D412 |
| Tensile strain | ASTM D412 | ||
| Fracture, 23 ℃ | 220 | % | ASTM D412 |
| Fracture, 23 ℃ | 130 | % | ASTM D412 |
| Fracture, 23 ℃ | 260 | % | ASTM D412 |
| Fracture, 23 ℃ | 300 | % | ASTM D412 |
| tear strength | |||
| 150℃ | 5.20 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 200℃，22 hr | 13 | % | ASTM D395B |
| 200℃，22 hr | 12 | % | ASTM D395B |
| 200℃，70 hr | 21 | % | ASTM D395B |
| 200℃，70 hr | 18 | % | ASTM D395B |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume change | ASTM D471 | ||
| 23 ℃, 168 hr, C-grade standard fuel | 5.9 | % | ASTM D471 |
| 23℃，168 hr，in M15（Fuel C/Methanol 85/15） | 15 | % | ASTM D471 |
| 23 ℃, 168 hr, methanol | 8.5 | % | ASTM D471 |
| 23 ℃, 168 hr, in water | 3.2 | % | ASTM D471 |
| 150 ℃, 168 hr, in ASTM 105 oil | 1.5 | % | ASTM D471 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 508 mm/min, Aged 70 hr at 275°C |
| 3. 508 mm/min, Aged 70 hr at 250°C |
| 4. 508 mm/min |
| 5. 20 in/min |
| 6. 20 in/min, Aged in ASTM 105 Oil for 168 hr at 302°F |
| 7. 20 in/min, Aged for 70 hr at 482°F |
| 8. 20 in/min, Aged for 70 hr at 527°F |
| 9. Die B |
| 10. Nicked |
| 11. Postcured for 2 hr at 232°C |
| 12. Aged in ASTM 105 Oil for 168 hr at 302°F |
| 13. Aged for 70 hr at 482°F |
| 14. Aged for 70 hr at 527°F |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |