| Product Description | |
|---|---|
| Supplier | USI |
| Generic | CBC |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.94 | g/cm³ | D792 |
| Water absorption rate | < 0.01 | % | D570 |
| Melt Flow Rate | |||
| 260 ℃，1.2 Kg | 54.6 | g/10 min | D1238 |
| 280 ℃，1.2 Kg | 136.3 | g/10 min | D1238 |
| 300 ℃，1.2 Kg | 296 | g/10 min | D1238 |
| melting point | 117 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| bending strength | 71.7 | MPa | D790 |
| Bending modulus | 2500 | MPa | D790 |
| tensile strength | |||
| yield | 33.7 | MPa | D638 |
| fracture | 32.9 | MPa | D638 |
| Tensile modulus | 2600 | MPa | D638 |
| Tensile strain | D638 | ||
| fracture | 3.7 | % | D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 29.5 | J/m | D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 117 | ℃ | D1525 |
| Hot deformation temperature | ℃ | ||
| 0.45 MPa | 102 | ℃ | D648 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |