| About |
|---|
| High temperature resistance Strength at elevated temperature Superior mechanical properties High compressive strength and creep resistance Excellent chemical resistance Superior resistance to plasma etching Outstanding electrical properties Wear resistance, low friction, self-lubricating Non-abrasive to mating parts Extremely low moisture absorption Radiation resistant Compliant without deforming under load and temperature Very low outgassing Zero metal and mineral extractables Extremely dimensionally stable Equal CTE in X, Y and Z directions&& |
| Product Description | |
|---|---|
| Generic | PI |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low extract,Good flexibility,Good Dimensional Stability,Good Electrical Properties,Gamma radiation,Low coefficient of friction,Machinable,Self-lubricating,High Heat Resistance,Low odor,Good wear resistance,Good compressive strength,Solvent resistance,Low moisture absorption |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| saturated | < 0.10 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD | 4.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+10 to 1.0E+11 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+12 to 1.0E+13 | ohms·cm | ASTM D257 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Spatial stability | |||
| Shrinkage, 24 hours, 260 ℃ | 0.0 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| E-level | 86 | ASTM D785 | |
| tensile strength | ASTM D638 | ||
| — | 70.9 | MPa | ASTM D638 |
| 260℃ | 58.5 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| fracture | 5.5 | % | ASTM D638 |
| Fracture, 260 ℃ | 3.7 | % | ASTM D638 |
| Bending modulus | 3150 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| — | 96.5 | MPa | ASTM D790 |
| 100% strain | 58.6 | MPa | ASTM D790 |
| Compression modulus | 2810 | MPa | ASTM D695 |
| compressive strength | ASTM D695 | ||
| 260℃ | 142 | MPa | ASTM D695 |
| 100% strain | 203 | MPa | ASTM D695 |
| Wear Rate – Jet Engine Simulation Testing，Bearing | |||
| 260℃ | 254.0 | µm | |
| 345℃ | 457.2 | µm | |
| 400℃ | 609.6 | µm |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 15 min soak |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |