| About |
|---|
| Vydyne 66J is a high-viscosity, heat-stabilized PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66J resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High Viscosity,Kosher certification,Grease resistance,Solvent resistance,Gasoline resistance,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃，2.0 mm | 2.0 | % | ISO 294-4 |
| MD：23℃，2.0 mm | 2.1 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 8.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 2.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2800 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 55.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 85.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | |||
| 23℃ | > 25 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3100 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 90.0 | MPa | ISO 178 |
| Poisson’s ratio | 0.40 | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 6.0 | kJ/m² | ISO 180 |
| 23℃ | 6.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 195 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 260 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃，2 mm | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃，2 mm | 1.0E-4 | 1/℃ | ISO 11359-2 |
| 0.71 mm | 140 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.71 mm | 95.0 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| 0.71 mm | 115 | ℃ | UL 746 |
| 1.5 mm | 125 | ℃ | UL 746 |
| 3.0 mm | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | |||
| 3.0 mm | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 400 to 599 | V | IEC 60112 |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.71 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.71 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 4 | UL 746 | |
| 3.0 mm | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.71 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.71 mm | 825 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 825 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 825 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.71 mm | 700 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 700 | ℃ | IEC 60695-2-13 |
| 3 mm | 700 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 250 to 295 | °C | |
| Barrel 2 zone temperature | 250 to 295 | °C | |
| Barrel 3 zone temperature | 250 to 295 | °C | |
| Barrel 4 zone temperature | 250 to 295 | °C | |
| Barrel 5 zone temperature | 250 to 295 | °C | |
| Melt temperature | 270 to 295 | °C | |
| Nozzle temperature | 270 to 295 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |