Vydyne® FR350J NT0727

About
Vydyne FR350J NT0727 is an unfilled, halogenated flame retardant PA66 designed to exceed the 775°C, zero flame, GWIT required for unattended appliance applications (IEC 60335-1). FR350J NT0727 exhibits excellent strength and ductility, allowing increased flexibility in product design. FR350J NT0727 provides enhanced flow and is lubricated for machine feed and easy mold release. It has an Underwriters Laboratories UL94 V-0 flame classification down to 0.4mm (0.016″) thick.&&

About

Vydyne FR350J NT0727 is an unfilled, halogenated flame retardant PA66 designed to exceed the 775°C, zero flame, GWIT required for unattended appliance applications (IEC 60335-1). FR350J NT0727 exhibits excellent strength and ductility, allowing increased flexibility in product design. FR350J NT0727 provides enhanced flow and is lubricated for machine feed and easy mold release. It has an Underwriters Laboratories UL94 V-0 flame classification down to 0.4mm (0.016″) thick.&&

Product Description
Supplier	Ascend
Generic	PA66
Material Status	Commercial: Active
Features	Good heat aging resistance,Good Electrical Properties,Corrosion Resistant,Good stripping performance,Flame Characteristics,Lubricating,Solvent resistance,Halogenated,Heat Stabilized,Homopolymer
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.31	g/cm³	ISO 1183
Water absorption rate
23℃，24hr	0.80	%
Equilibrium, 23 ℃, 50% RH	1.9	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	3200	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	70.0	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	15	%	ISO 527-2
Bending modulus
23℃	3200	MPa	ISO 178
bending strength
23℃	90.0	MPa	ISO 178
Poisson’s ratio	0.40		ISO 527-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	4.3	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	65	kJ/m²	ISO 179/1eU
Impact strength of cantilever beam notch
23℃	4.1	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	90.0	℃	ISO 75-2/A
Melting temperature	265	℃	ISO 11357-3
0.40 mm	130	℃
0.75 mm	130	℃
1.5 mm	130	℃
3.0 mm	130	℃
Relative temperature index
Electrical performance
0.40 mm	110	℃
0.75 mm	110	℃
1.50 mm	110	℃
3.00 mm	110	℃

Electrical performance	Nominal value	Unit	Test method
Volume resistivity
0.75 mm	1.0E+18	ohms·cm	IEC 60093
Dielectric strength
1 mm	17	kV/mm	IEC 60243
Compared to the leakage tracing index
3.00 mm	250 to 399	V	IEC 60112
High Arc Burning Index (HAI)
0.40 mm	PLC 0
0.75 mm	PLC 0
1.5 mm	PLC 0
3.0 mm	PLC 0
Hot wire ignition
HWI
0.40 mm	PLC 0
0.75 mm	PLC 0
1.5 mm	PLC 0
3.0 mm	PLC 0

FLAME CHARACTERISTICS	Nominal value	Unit
Flame retardant level
0.40 mm	V-0
0.75 mm	V-0
1.50 mm	V-0
3.00 mm	V-0
Glowing wire flammability index
0.40 mm	960	℃
0.75 mm	960	℃
1.5 mm	960	℃
3.0 mm	960	℃
Igniting temperature of the hot wire
0.4 mm	960	℃
0.75 mm	960	℃
1.5 mm	960	℃
3 mm	960	℃

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Proposed maximum recycled material ratio	50	%
Barrel rear temperature	260 to 290	°C
Barrel middle temperature	260 to 290	°C
Barrel front temperature	260 to 290	°C
Nozzle temperature	260 to 290	°C
Processing (melt) temperature	270 to 285	°C
Mold temperature	65 to 95	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.