| Hostacom X 454是一种聚丙烯共聚物(PP Copoly)产品,。 它,在非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Hostacom X 454的应用领域包括汽车行业 和 工程/工业配件。 主要特性为:共聚物。&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Copolymer,HB |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃，2.0 mm | 1.0 | % | ISO 294-4 |
| MD：23℃，2.0 mm | 0.50 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.2 | % | ISO 62 |
| 23℃，24hr | 1.0 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 6600 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 120 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 5900 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 170 | MPa | ISO 178 |
| Poisson’s ratio | 0.40 | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 6.0 | kJ/m² | ISO 179 |
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 32 | kJ/m² | ISO 179 |
| 23℃ | 39 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 5.7 | kJ/m² | ISO 180 |
| 23℃ | 6.6 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 241 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 258 | ℃ | ISO 75-2/B |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃，2 mm | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃，2 mm | 3.0E-5 | 1/℃ | ISO 11359-2 |
| 0.75 mm | 140 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 120 | ℃ | UL 746 |
| 1.5 mm | 120 | ℃ | UL 746 |
| 3.0 mm | 120 | ℃ | UL 746 |
| 0.75 mm | 125 | ℃ | UL 746 |
| 1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm | 140 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 0.75 mm | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 20 | kV/mm | IEC 60243 |
| Arc resistance | |||
| 3.0 mm | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 250 to 399 | V | IEC 60112 |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.75 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 3 | UL 746 | |
| 3.0 mm | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.75 mm | 675 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 675 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 675 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.75 mm | 700 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 700 | ℃ | IEC 60695-2-13 |
| 3 mm | 700 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 280 to 310 | °C | |
| Barrel middle temperature | 280 to 310 | °C | |
| Barrel front temperature | 280 to 310 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 285 to 305 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |