Vydyne® R530H BK0201

About
Vydyne R530H BK0201 is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved machine feed and flow. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R530H BK0201 is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R530H BK0201 has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End Uses: Vydyne R530H BK0201 has been used for several under-the-hood automotive applications. The hydrolysis-resistant properties make it an excellent candidate for radiator end tank and heater core applications.&&

About

Vydyne R530H BK0201 is general-purpose, heat-stabilized, hydrolysis-resistant, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved machine feed and flow. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R530H BK0201 is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R530H BK0201 has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End Uses: Vydyne R530H BK0201 has been used for several under-the-hood automotive applications. The hydrolysis-resistant properties make it an excellent candidate for radiator end tank and heater core applications.&&

Product Description
Supplier	Ascend
Generic	PA66
Material Status	Commercial: Active
Features	Hydrolysis stability,Good liquidity,Antifreeze,Lubricating,Fatigue resistance,Solvent resistance,Gasoline resistance,Heat Stabilized
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.37	g/cm³	ISO 1183
Shrinkage rate			ISO 294-4
TD：23℃，2.0 mm	0.90	%	ISO 294-4
MD：23℃，2.0 mm	0.40	%	ISO 294-4
Water absorption rate
Balance, 50% RH	1.9	%	ISO 62
23℃，24hr	0.90	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	10000	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	195	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	3.0	%	ISO 527-2
Bending modulus
23℃	9600	MPa	ISO 178
bending strength
23℃	270	MPa	ISO 178
Poisson’s ratio
23℃	0.40		ISO 527

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-30℃	9.5	kJ/m²	ISO 179
23℃	11	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-30℃	65	kJ/m²	ISO 179
23℃	75	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
-30℃	10	kJ/m²	ISO 180
23℃	12	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	260	℃	ISO 75-2/A
0.45 MPa, unannealed	250	℃	ISO 75-2/B
Melting temperature	260	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃，2 mm	1.1E-4	1/℃	ISO 11359-2
MD：23~55℃，2 mm	2.2E-5	1/℃	ISO 11359-2

Electrical performance	Nominal value	Unit	Test method
Volume resistivity
3.0mm	1.0E+13	ohms·cm	IEC 60093
Dielectric strength
1.0mm	20	kV/mm	IEC 60243
Arc resistance
3.0mm	PLC6		ASTM D495
Compared to the leakage tracing index
3.0mm	250-399	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
0.75mm	HB	UL 94
1.5mm	HB	UL 94
3.0mm	HB	UL 94

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	80.0	°C
Drying time	4.0	hr
Suggested maximum proportion of recycled materials	25	%
Temperature at the rear of the barrel	280 to 310	°C
Temperature in the middle of the barrel	280 to 310	°C
Front temperature of material barrel	280 to 310	°C
Nozzle temperature	280 to 310	°C
Processing (melt) temperature	285 to 305	°C
Mold temperature	65.0 to 95.0	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.