| About |
|---|
| Vydyne R533 NAT is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R533 NAT resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-fiber reinforced PA66 resins over aluminum and/or zinc die-cast parts.&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good Electrical Properties,Good liquidity,Corrosion Resistant,Good stripping performance,Non-corrosiveness,Lubricating,Solvent resistance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.90 | % | ISO 294-4 |
| MD | 0.40 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，50% RH | 1.70 | % | ISO 62 |
| 23℃，24hr | 0.80 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 250 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/Bf |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD | 2.1E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.00 mm | 20 | KV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| All color | 0.75mm | HB | UL-94 |
| All color | 1.50mm | HB | UL-94 |
| All color | 3.00mm | HB | UL-94 |
| Igniting temperature of the hot wire | |||
| 3 mm | 750 | ℃ | IEC 60695-2-13 |
| 3 mm | 675 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 675 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 725 | ℃ | IEC 60695-2-13 |
| 0.75 mm | 775 | ℃ | IEC 60695-2-13 |
| Relative temperature of heating wire | |||
| 3.00mm | 700 | ℃ | IEC 60695-2-12 |
| 3.00mm | 800 | ℃ | IEC 60695-2-12 |
| 1.50mm | 700 | ℃ | IEC 60695-2-12 |
| 1.50mm | 725 | ℃ | IEC 60695-2-12 |
| 0.75mm | 750 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 70-80 | °C | |
| Drying time | 4.0-12 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 250-280 | °C | |
| Barrel middle temperature | 260-290 | °C | |
| Barrel front temperature | 270-300 | °C | |
| Nozzle temperature | 270-310 | °C | |
| Mold temperature | 60-140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |