Vydyne® R533H

About

Product Description
Supplier	Ascend
Generic	PA66
Material Status	Commercial: Active
Features	Heat Stabilized,High liquidity,Lubricating,Good stripping performance,Good Rigidity,HB
Availabilitys	Europe,North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.40	g/cm³	ISO 1183
Shrinkage rate			ISO 294-4
TD：23℃，2.0 mm	0.90	%	ISO 294-4
MD：23℃，2.0 mm	0.40	%	ISO 294-4
Water absorption rate
Equilibrium, 23 ℃, 50% RH	1.8	%	ISO 62
23℃，24hr	0.80	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	10200	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	205	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	3.0	%	ISO 527-2
Bending modulus
23℃	9700	MPa	ISO 178
bending strength
23℃	290	MPa	ISO 178
Poisson’s ratio	0.40		ISO 527-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-30℃	12	kJ/m²	ISO 179
23℃	12	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-30℃	75	kJ/m²	ISO 179
23℃	85	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
23℃	12	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	250	℃	ISO 75-2/A
0.45 MPa, unannealed	260	℃	ISO 75-2/B
Melting temperature	260	℃	ISO 3146
Vicat Softening Temp	252	℃	ISO 360/B
Linear coefficient of thermal expansion
TD：23~55℃，2 mm	9.0E-6	1/℃	ISO 11359-2
MD：23~55℃，2 mm	2.0E-6	1/℃	ISO 11359-2
Relative temperature index
Electrical performance
0.75 mm	140	℃	UL 746
1.50 mm	140	℃	UL 746
3.00 mm	140	℃	UL 746
Impact mechanical performance
0.75 mm	125	℃	UL 746
1.50 mm	125	℃	UL 746
3.00 mm	125	℃	UL 746
Non mechanical impact performance
0.75 mm	140	℃	UL 746
1.50 mm	140	℃	UL 746
3.00 mm	140	℃	UL 746

Electrical performance	Nominal value	Unit	Test method
Volume resistivity
0.75 mm	1.0E+13	ohms·cm	IEC 60093
Dielectric strength
23 ℃，3 mm	16	kV/mm	IEC 60243-1
Arc resistance
3.0 mm	PLC6		ASTM D495
Compared to the leakage tracing index
3.00 mm	PLC2		UL 746
3.00 mm	400to599	V	IEC 60112
High Arc Burning Index (HAI)			UL 746
0.75mm	PLC 0		UL 746
1.5mm	PLC 0		UL 746
3.0mm	PLC 0		UL 746
High voltage arc marking rate
HVTR	PLC 1		UL 746
Hot wire ignition
0.75mm	PLC 4		UL 746
1.5mm	PLC 3		UL 746
3.0mm	PLC 4		UL 746
HWI			UL 746

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 94
0.75 mm	HB		UL 94
1.50 mm	HB		UL 94
3.00 mm	HB		UL 94
Oxygen index	28	%	ASTM D2863

Process Conditions
Injection	Nominal value	Unit	Test method
drying temperature	70	°C
Drying time	3.0	hr
Suggested injection size	40-80	%
Suggested maximum proportion of recycled materials	25	%
Temperature at the rear of the barrel	280 to 310	°C
Temperature in the middle of the barrel	280 to 310	°C
Front temperature of material barrel	280 to 310	°C
Nozzle temperature	280 to 310	°C
Processing (melt) temperature	285 to 305	°C
Mold temperature	65 to 95	°C
Injection pressure	55 to 140	MPa
Injection rate	快速
Maintain pressure	55 to 140	MPa

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.