| About |
|---|
| Vydyne R550 is general-purpose, hydrolysis-resistant, 50% glass-fiber reinforced PA66 resin. Available in natural, it is also lubricated for improved flow and offers superior surface appearance. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Hydrolysis stability,Good liquidity,Good stripping performance,Lubricating,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃，2.0 mm | 0.90 | % | ISO 294-4 |
| MD：23℃，2.0 mm | 0.40 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 1.2 | % | ISO 62 |
| 23℃，24hr | 0.50 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 16800 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 240 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 16000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 350 | MPa | ISO 178 |
| Poisson’s ratio | 0.40 | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 14 | kJ/m² | ISO 179/1eA |
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 91 | kJ/m² | ISO 179/1eU |
| 23℃ | 95 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | ISO 180 | ||
| -30℃ | 16 | kJ/m² | ISO 180 |
| 23℃ | 17 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 255 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 260 | ℃ | ISO 75-2/B |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD：23~55℃，2 mm | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD：23~55℃，2 mm | 1.2E-5 | 1/℃ | ISO 11359-2 |
| 0.75 mm | 125 | ℃ | UL 746 |
| 1.5 mm | 125 | ℃ | UL 746 |
| 3.0 mm | 125 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 0.75 mm | 110 | ℃ | UL 746 |
| 1.5 mm | 110 | ℃ | UL 746 |
| 3.0 mm | 110 | ℃ | UL 746 |
| 0.75 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 0.75 mm | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 22 | kV/mm | IEC 60243 |
| Arc resistance | |||
| 3.0 mm | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | |||
| 3.00 mm | 600 | V | IEC 60112 |
| High Arc Burning Index (HAI) | UL 746 | ||
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.75 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 4 | UL 746 | |
| 3.0 mm | PLC 4 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.75 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Automotive materials | |||
| thickness d = 1mm | + | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Proposed maximum recycled material ratio | 25 | % | |
| Barrel rear temperature | 280 to 310 | °C | |
| Barrel middle temperature | 280 to 310 | °C | |
| Barrel front temperature | 280 to 310 | °C | |
| Nozzle temperature | 280 to 310 | °C | |
| Processing (melt) temperature | 285 to 305 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |