| Vyncolit® X7012 is a glass fiber and glass beads reinforced molding compound with high mechanical strength, even at high temperatures in Long Life Coolants.&& |
| Product Description | |
|---|---|
| Supplier | SBHPP |
| Generic | 酚醛树脂 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,V-0 |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.60 | g/cm³ | ISO 1183 |
| Apparent density | 0.64 | g/cm³ | ISO 60 |
| Shrinkage rate | 0.35 | % | ISO 2577 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.080 | % | ISO 62 |
| Post contraction | 0.090 | % | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 13000 | MPa | ISO 527-2 |
| tensile strength | 100 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 0.80 | % | ISO 527-2 |
| Bending modulus | 12000 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| compressive strength | 260 | MPa | ISO 604 |
| Fracture bending strain | 1.6 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.8 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 13 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 213 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | TMA | ||
| MD | 1.9E-5 | 1/℃ | TMA |
| TD | 5.5E-5 | 1/℃ | TMA |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |