| About |
|---|
| Vyteen ABS 2904 is a black recycled ABS high impact high flow terpolymer with balanced impact/stiffness properties designed for injection molding applications Features Excellent resilience Good processability High Stiffness Typical Applications Automotive MS DB200 compliance Appliances housing Electrical components&& |
| Product Description | |
|---|---|
| Supplier | Lavergne |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,High liquidity,Elastic,Terpolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.05 | g/cm³ | ASTM D792 |
| 23℃ | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 7.0 | g/10min | ASTM D1238 |
| 230℃，3.80kg | 7.0 | g/10min | ISO 1133 |
| Shrinkage rate | ASTM D955 | ||
| MD | 0.50 | % | ASTM D955 |
| TD | 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | ||
| -30℃ | 7.0 | kJ/m² | ISO 179/eA |
| 23℃ | 15 | kJ/m² | ISO 179/eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 170 | J/m | ASTM D256 |
| Drop hammer impact | ASTM D5420 | ||
| -29℃ | 4.00 | J | ASTM D5420 |
| 23℃ | 15.0 | J | ASTM D5420 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 80.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 86.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | 45 | mm/min | SAE J369 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 85 | ASTM D785 | |
| Tensile modulus | 2000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 36.0 | MPa | ASTM D638 |
| yield | 35.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| — | 2100 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| bending strength | |||
| — | 62.0 | MPa | ASTM D790 |
| — | 58.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Recommended maximum moisture content | 0.30 | % | |
| Barrel rear temperature | 185 to 195 | °C | |
| Barrel middle temperature | 200 to 210 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 230 to 240 | °C | |
| Processing (melt) temperature | 220 to 235 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Injection speed | 中等偏快 | ||
| Screw speed | 60 to 90 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.051 in/min |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |