| About |
|---|
| 120-PHLY is a semi-transparent flexible material. The material has excellent mechanical properties, excellent low temperature toughness, UV resistance, yellowing resistance, hydrolysis resistance. |
| Product Description | |
|---|---|
| Supplier | Worldful |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Hydrolysis stability,Low temperature toughness,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 240℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.80 to 1.2 | % | |
| TD | 0.90 to 1.4 | % | |
| Water absorption rate | |||
| balance | 0.70 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | 25.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| Bending modulus | 500 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | No Break | ASTM D256 | |
| Impact strength of cantilever beam notch | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | |
| 1.8 MPa, unannealed | 45.0 | ℃ | |
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 5 |
| Melting temperature | 175 | ℃ | ASTM D2133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 34 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 170 to 190 | °C | |
| Temperature in the middle of the barrel | 190 to 220 | °C | |
| Front temperature of material barrel | 180 to 200 | °C | |
| Processing (melt) temperature | 180 to 210 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 1.00 to 3.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |