| About |
|---|
| K900CF-MV is a 20% carbon fiber reinforced Polyetheretherketone with medium viscosity. The material has excellent wear resistance, chemical resistance, high strength, high heat resistance and dimensional stability. |
| Product Description | |
|---|---|
| Supplier | Worldful |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,High Heat Resistance,Good wear resistance,Solvent resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 380℃，5.0kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | |
| TD | 0.60 to 0.90 | % | |
| Water absorption rate | |||
| balance | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 400 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 80 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 334 | ℃ | |
| 1.8 MPa, unannealed | 325 | ℃ | |
| Vicat Softening Temp | 335 | ℃ | ASTM D1525 5 |
| Melting temperature | 343 | ℃ | ASTM D2133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+7 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| Tensile strength | 205 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 16000 | MPa | ASTM D790 |
| bending strength | 310 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 140 to 170 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 360 to 390 | °C | |
| Temperature in the middle of the barrel | 380 to 410 | °C | |
| Front temperature of material barrel | 380 to 400 | °C | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 150 to 200 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 2.00 to 3.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |