| A900GF30F-GN is a 30% glass fiber reinforced halogen-free, phosphorus-free flame-retardant PPA rated flame retardant, high strength, excellent heat resistance, and good dimensional stability. |
| Product Description | |
|---|---|
| Supplier | Worldful |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Halogen free,Flame Characteristics,High Heat Resistance,Low to no phosphorus content |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | |
| TD | 0.30 to 0.60 | % | |
| Water absorption rate | |||
| balance | 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | > 400 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 280 | ℃ | |
| 1.8 MPa, unannealed | 270 | ℃ | |
| Vicat Softening Temp | 270 | ℃ | ASTM D1525 5 |
| Melting temperature | 315 | ℃ | ASTM D2133 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 27 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 550 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| Tensile strength | 150 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.2 | % | ASTM D638 |
| Bending modulus | 10600 | MPa | ASTM D790 |
| bending strength | 250 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 to 150 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 260 to 280 | °C | |
| Temperature in the middle of the barrel | 290 to 320 | °C | |
| Front temperature of material barrel | 280 to 310 | °C | |
| Processing (melt) temperature | 290 to 300 | °C | |
| Mold temperature | 110 to 150 | °C | |
| Injection speed | 慢to中等 | ||
| Back pressure | 1.00 to 2.00 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |