| About |
|---|
| Glass Sphere Reinforced Nylon Resin (PA6)&& |
| Product Description | |
|---|---|
| Supplier | Wellman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD：23℃ | 1.0 to 1.4 | % | ISO 294-4 |
| MD：23℃ | 1.1 to 1.5 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 70.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 10 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 4500 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 110 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 220 | ℃ | ISO 3146 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 271 to 282 | °C | |
| Barrel middle temperature | 266 to 277 | °C | |
| Barrel front temperature | 260 to 271 | °C | |
| Nozzle temperature | 254 to 277 | °C | |
| Processing (melt) temperature | 249 to 277 | °C | |
| Mold temperature | 71 to 93 | °C | |
| Injection pressure | 34.5 to 138 | MPa | |
| Back pressure | 0.345 | MPa | |
| Screw speed | 30 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |