WELLAMID Nylon 6000/42 GS 30 HWCP

About
WELLAMID Nylon 6000/42 GS 30 HWCP is a Polyamide 6 (Nylon 6) material filled with 30% glass bead. It is available in Europe. Important attributes of WELLAMID Nylon 6000/42 GS 30 HWCP are: Flame Rated Heat Stabilizer Impact Modified&&

Product Description
Generic	PA6
Material Status	Commercial: Active
Features	Heat Stabilized,High impact resistance
Availabilitys	Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile Strain
Broken BRK, dry dry	7	MPa	ISO 527
Broken BRK, wet Cond	20	MPa	ISO 527
Tensile Strength
Dry	52	%	ISO 527-2
Wet Cond	35	%	ISO 527-2
Tensile Modulus
Dry	3100	MPa	ISO 527
Wet Cond	1300	MPa	ISO 527
Flexural Modulus	2600	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23 ℃, dry	50	kJ/m²	ISO 179
23 ℃, moist cond	80	kJ/m²	ISO 179
Charpy Unnotch Impact strength
23 ℃, dry	7	kJ/m²	ISO 179
23 ℃, moist cond	17	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Melting temperature	223	℃
Hot deformation temperature HDT
A	70	℃	ISO 75-1/-2
B	180	℃	ISO 75-1/-2
Vicat Softening Temperature	200	℃	ISO 306/B
Coeff. of linear thermal expansion
23℃-80℃	0.35	×10-4/K	DIN 53752

ELECTRICAL	Nominal value	Unit	Test method
Relative permittivity
Dry	4	1 MHz	IEC 60250
Wet Cond	6	1 MHz	IEC 60250
Dissipation Factor
Dry	200	1 MHz	IEC 60250
Wet Cond	2000	1 MHz	IEC 60250
Electric strength
Dry	35	kV/mm	IEC 60243-1
Wet Cond	35	kV/mm	IEC 60243-1
Compared Tracking Index
Dry	450	V	IEC 60112
Volume Resistance
Dry	1E15	ohm·cm	IEC 60093
Wet Cond	1E12	ohm·cm	IEC 60093
Surface Resistivity
Dry	1E12	ohm	IEC 60093
Wet Cond	1E10	ohm	IEC 60093

PHYSICAL	Nominal value	Unit	Test method
Density	1.33	g/cm³	ISO 1183
Mold Shrinkage	0.8-1	%
Saturation value at	1.5-2	%	DIN 53495

FLAME CHARACTERISTICS	Nominal value	Test method
Flame Class Rating
1.6 mm	HB	UL 94
1.6 mm	HB	UL 94
3.2 mm	HB	UL 94
3.2 mm	HB	UL 94

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Melt Temperature	250 to 270	°C
Mold Temperature	60 to 90	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.