| AXIALLu0027s Georgia Gulf 5009 is a type I, Grade I rigid vinyl injection molding compound designed for fittings and parts of similar configuration where maximum tensile strength and/or chemical resistance is required. It has full NSF approval and is suitable for all types of water distribution systems, including pressure fittings. |
| Product Description | |
|---|---|
| Supplier | Westlake Chemical |
| Generic | PVC，刚硬 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Solvent resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| TD | 0.20 to 0.40 | % | ASTM D955 |
| PVC unit classification | 12454-B | ASTM D1784 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -20℃，6.4mm | 32 | J/m | |
| 23℃，6.4mm | 43 | J/m | |
| Drop hammer impact | |||
| 23℃ | 36.2 | J | ASTM D3029 |
| Falling impact resistance (23 ° C) | 116 | J/cm | ASTM D4226 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 74.0 | ℃ | |
| 1.8 MPa, unannealed | 70.0 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 38 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | 2760 | MPa | ASTM D638 |
| Tensile strength | 48.3 | MPa | ASTM D638 |
| Bending modulus | 2690 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 66 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 6.0 | hr | |
| Suggested injection volume | 35 to 75 | % | |
| Suggested maximum proportion of recycled materials | 50 | % | |
| Temperature at the rear of the barrel | 163 | °C | |
| Temperature in the middle of the barrel | 174 to 191 | °C | |
| Front temperature of material barrel | 182 to 193 | °C | |
| Nozzle temperature | 177 to 193 | °C | |
| Processing (melt) temperature | 202 to 210 | °C | |
| Mold temperature | 16 to 49 | °C | |
| Injection pressure | 82.7 to 138 | MPa | |
| Maintaining pressure | 48.3 to 82.7 | MPa | |
| Back pressure | 0.345 to 1.38 | MPa | |
| Screw speed | 25 to 80 | rpm | |
| Locking force | 3.4 | kN/cm² | |
| Screw length to diameter ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw compression ratio | 1.5:1.0 to 2.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |