| About |
|---|
| WONDERLITE® PC-122 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant High Flow&& |
| Product Description | |
|---|---|
| Supplier | CHI MEI |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good liquidity,V-2 |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 22 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 22.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 60 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 820 | J/m | ASTM D256 |
| 23℃ | 60 | kJ/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 143 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 128 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 144 | ℃ | ASTM D648 |
| Vicat Softening Temp | 150 | ℃ | ASTM D1525 7 |
| Vicat Softening Temp | |||
| A50 | 150 | ℃ | ISO 306/A50 |
| B50 | 145 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 to 8.0E-5 | 1/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.38 mm | V-2 | UL 94 | |
| 3.20 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2/50 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| yield | 61.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 120 | % | ISO 527-2/50 |
| fracture | 110 | % | ASTM D638 |
| Bending modulus | 2340 | MPa | ASTM D790 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 89.8 | MPa | ASTM D790 |
| bending strength | 90.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 77 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 220 to 300 | °C | |
| Barrel middle temperature | 240 to 310 | °C | |
| Barrel front temperature | 240 to 300 | °C | |
| Mold temperature | 70 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 0.24 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. 132°C x 8 hr |
| 7. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |