| Supplier | CHI MEI |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Antifreeze,Flame Characteristics |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 260℃，5.0kg | 13 | g/10min | ISO 1133 |
| Shrinkage rate | 0.4~0.6 | % | ISO 2577 |
| Density | |||
| 23℃ | 1.18 | g/cm³ | ISO 1183 |
| Dielectric constant | |||
| 1 MHz | 3.1 | IEC 60250 | |
| Volumetric resistance | 3.9E+15 | Ohm*m | IEC 60093 |
| Surface resistivity | 2.9E+15 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm | 5VB | UL 94 | |
| 3.00 mm | 5VA | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy impact strength | |||
| 3.2mm,4mm/23℃ | 55 | kJ/m² | ISO 179 |
| 3.2mm,4mm/-30℃ | 16 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm，4mm | 55 | kJ/m² | ISO 180 |
| -30℃，3.2mm，4mm | 16 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 112 | ℃ | ISO 306 |
| B50 | 105 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 86 | ℃ | ISO 75 |
| 0.45 MPa, unannealed | 95 | ℃ | ISO 75 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |