| WPP PP PPH2TF2-Black is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include: Heat Stabilizer Homopolymer&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| 230℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 32.0 | MPa | ASTM D638 |
| yield | 37.0 | MPa | ISO 527-2/5 |
| yield | 33.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 9.0 | % | ASTM D638 |
| yield | 10 | % | ISO 527-2/5 |
| Bending modulus | 2300 | MPa | ASTM D790 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 46.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 32 | J/m | ASTM D256 |
| 23℃ | 600 | J/m | ASTM D256 |
| 23℃ | 3.0 | kJ/m² | ISO 180 |
| 23℃ | 5.0 | kJ/m² | ISO 180-1B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 95.0 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 71.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 111 | ℃ | ISO 75-2/B |
| 0.45 MPa, unannealed | 124 | ℃ | ASTM D648 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.050 in/min |
| 4. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |