| About |
|---|
| WPP PP PPH4GF3-Black is a Polypropylene Homopolymer (PP Homopolymer) product filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of WPP PP PPH4GF3-Black include automotive and consumer goods. Characteristics include: Good Dimensional Stability Good Stiffness High Strength Homopolymer&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Good Tensile Strength,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 84.0 | MPa | ISO 527-2/5 |
| Bending modulus | 5600 | MPa | ISO 178 |
| bending strength | 134 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 43 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| -40℃ | 7.0 | kJ/m² | ISO 180 |
| 23℃ | 8.0 | kJ/m² | ISO 180 |
| 23℃ | 8.0 | kJ/m² | ISO 180-1B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 149 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 158 | ℃ | ISO 75-2/B |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |