| About |
|---|
| Extremely Low Viscosity, Molding Release&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good stripping performance,V-2 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | |||
| 23℃ | 60 | kJ/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 130 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD | 6.5E-5 | 1/℃ | ISO 11359-2 |
| 0.75 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| 3.0 mm | 130 | ℃ | UL 746 |
| 0.75 mm | 125 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 29 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 6.6E-4 | IEC 60250 | |
| 1 MHz | 9.2E-3 | IEC 60250 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.75 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-2 | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 800 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 875 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| Rockwell hardness | |||
| M-level | 70 | ISO 2039-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 23.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Limiting Viscosity Number | 43.0 | cm³/g | ISO 1628-4 |
| Thermal Conductivity of Melt | 0.24 | W/m/K |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |