| Very Low Viscosity, UV Stabilized, Molding Release&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low Viscosity,Good stripping performance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 24 hours | 0.35 | % | ISO 62 |
| Characteristic viscosity | 1270 | in³/lb | ISO 1628-4 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 0.976 | in³/10min | ISO 1133 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 89.0 | % | ISO 13468-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 130 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 145 | ℃ | ISO 306 |
| Ball pressure test | Pass | IEC 60695-10-2 | |
| Thermal conductivity coefficient | 1.7 | Btu·in/hr/ft²/°F | |
| Linear coefficient of thermal expansion | |||
| MD | 3.6E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | >1.0E+15 | Ω.cm | IEC 60093 |
| Surface resistance | >1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 740 | KV/mm | IEC 60243-1 | |
| Dielectric constant | |||
| 2.90 | 1 MHz | IEC 60250 | |
| 3.00 | 100 Hz | IEC 60250 | |
| Dissipation factor | |||
| 9.2E-3 | IEC 60250 | ||
| 6.6E-4 | 100 Hz | IEC 60250 | |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 69.3 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 70 | M 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 60 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | >50 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2305 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 90 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2400 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |