| About |
|---|
| Laser Direct Structuring (LDS)*, Flame Retardant (Halogen free), HIgh Flow, Black color only *The compound is intended specifically for the use in the process of manufacturing conducting path designs according to the German application of the patent 101 32 092 of LPKF Laser & Electronics AG. Please address straight to LPKF Laser & Electronics AG (www.LPKF.de).&& |
| Product Description | |
|---|---|
| Supplier | Mitsubishi |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity,Halogen free,Flame Characteristics,V-1 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 28.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.60 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.35 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 60.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 5.0 | % | ISO 527-2 |
| Nominal tensile fracture strain | > 50 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 20 | kJ/m² | ISO 179/1eA |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | No Break | ISO 179/1eU | |
| 23℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/4A | ||
| -20℃ | 20 | kJ/m² | ISO 180-4A |
| 23℃ | 55 | kJ/m² | ISO 180-4A |
| Multi axial instrumented impact energy | |||
| -20℃ | 25.0 | J | Internal Method |
| 23℃ | 40.0 | J | ISO 6603-2 |
| 23℃ | 25.0 | J | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 103 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 110 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1.00 GHz | 3.00 | IEC 60250 | |
| Dissipation factor | |||
| 1 GHz | 5.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.60 mm | V-1 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-1 | IEC 60695-11-10, -20 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Part with rib, Based on ISO 6603-2 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |