| About |
|---|
| 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Ductility,Hypocrystalline,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | ASTM D792 |
| Specific volume | 0.700 | cm³/g | ASTM D792 |
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 24 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，5 kg | 12.0 | cm³/10min | ISO 1133 |
| 265℃，5 kg | 19.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.30 to 0.40 | % | Internal Method |
| MD | 0.40 to 0.50 | % | Internal Method |
| TD | 0.40 to 0.70 | % | Internal Method |
| TD | 0.70 to 0.90 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.50 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| 24hr | 0.090 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 640 | J/m | ASTM D256 |
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 170 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| -30℃ | 6.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Energy at Peak Load | 5.00 | J | ASTM D3763 |
| 23℃，Total Energy | 17.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 155 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 6.4 mm | 204 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 163 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 149 | ℃ | ASTM D648 |
| Vicat Softening Temp | 153 | ℃ | ASTM D1525 12 |
| Vicat Softening Temp | |||
| B50 | 148 | ℃ | ISO 306 |
| B120 | 150 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.1E-4 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 2.7E-5 | 1/℃ | ISO 11359-2 |
| MD: -40 to 40 ℃ | 2.7E-5 | cm/cm/℃ | ASTM E831 |
| 60 to 138 ℃ | 2.0E-5 | cm/cm/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 140 | ℃ | UL 746 |
| Strength mechanical performance | 140 | ℃ | UL 746 |
| Impact mechanical performance | 130 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 4.8E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 1.6 mm in oil | 27 | kV/mm | ASTM D149 |
| 3.2 mm in air | 20 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 100 Hz | 4.00 | ASTM D150 | |
| 1 MHz | 4.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 100 Hz | 3.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 | |
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 3 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 1 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9750 | MPa | ASTM D638 |
| Tensile modulus | 8500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 3.00 | MPa | ISO 527-2/5 |
| fracture | 91.0 | MPa | ASTM D638 |
| yield | 97.0 | MPa | ASTM D638 |
| yield | 105 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 110 | % | ISO 527-2/5 |
| fracture | 4.0 | % | ASTM D638 |
| yield | 3.0 | % | ISO 527-2/5 |
| yield | 3.0 | % | ASTM D638 |
| Bending modulus | |||
| — | 7750 | MPa | ISO 178 |
| 50 mm span | 5380 | MPa | ASTM D790 |
| bending strength | 154 | MPa | ISO 178 |
| bending strength | |||
| Fracture, 50 mm span | 138 | MPa | ASTM D790 |
| Yield, 50 mm span | 150 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 109 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 50 to 80 | % | |
| Barrel rear temperature | 249 to 271 | °C | |
| Barrel middle temperature | 254 to 277 | °C | |
| Barrel front temperature | 260 to 282 | °C | |
| Nozzle temperature | 254 to 277 | °C | |
| Processing (melt) temperature | 260 to 282 | °C | |
| Mold temperature | 66 to 93 | °C | |
| Back pressure | 0.345 to 0.552 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Vent depth | 0.013 to 0.020 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.75 to 2.3 mm |
| 3. 2.3 to 4.6 mm |
| 4. 0.20 in/min |
| 5. Type I, 0.20 in/min |
| 6. 0.051 in/min |
| 7. 0.079 in/min |
| 8. Yield |
| 9. 80*10*4 sp=62mm |
| 10. 80*10*4 |
| 11. 80*10*4 mm |
| 12. Rate B (120°C/h), Loading 2 (50 N) |
| 13. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |