| About |
|---|
| PBT+PC, Unfilled, Impact Modified, UV stabilized. Outstanding low temperature impact performance and chemical resistance.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Solvent resistance,low-temperature impact resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Specific volume | 0.835 | cm³/g | ASTM D792 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 266℃，5.0kg | 22 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 17.1 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 1.6 to 1.8 | % | Internal Method |
| MD：3.2 mm | 1.6 to 1.8 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.14 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1780 | MPa | ASTM D638 |
| Tensile modulus | 1830 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 31.7 | MPa | ISO 527-2/50 |
| fracture | 32.9 | MPa | ASTM D638 |
| yield | 43.7 | MPa | ASTM D638 |
| yield | 41.1 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 19 | % | ISO 527-2/50 |
| fracture | 150 | % | ASTM D638 |
| yield | 3.9 | % | ISO 527-2/50 |
| yield | 4.2 | % | ASTM D638 |
| Bending modulus | 1700 | MPa | ISO 178 |
| 50 mm span | 1780 | MPa | ASTM D790 |
| bending strength | 60.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 63.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 72 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 670 | J/m | ASTM D256 |
| 23℃ | 900 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| 23℃ | 1600 | J/m | ASTM D4812 |
| -30℃ | 51 | kJ/m² | ISO 180-1A |
| 23℃ | 54 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 56.3 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 50.5 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 6.4 mm | 60.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 98.9 | ℃ | ASTM D648 |
| Vicat Softening Temp | 123 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 119 | ℃ | ISO 306 |
| B120 | 122 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.0E-4 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 9.9E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 9.9E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | |||
| Electrical performance | 75.0 | ℃ | UL 746 |
| Strength mechanical performance | 75.0 | ℃ | UL 746 |
| Impact mechanical performance | 75.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 5 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 1 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 104 to 116 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Drying time, maximum | 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 50 to 80 | % | |
| Barrel rear temperature | 232 to 246 | °C | |
| Barrel middle temperature | 241 to 254 | °C | |
| Barrel front temperature | 249 to 266 | °C | |
| Nozzle temperature | 249 to 271 | °C | |
| Processing (melt) temperature | 249 to 271 | °C | |
| Mold temperature | 38 to 82 | °C | |
| Back pressure | 0.172 to 0.345 | MPa | |
| Vent depth | 0.013 to 0.020 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 11. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |