| About |
|---|
| XENOY™ CL100 resin XENOY CL100 is an unfilled, impact modified, UV-stabilized PC/PBT blend with excellent solvent resistance and good low-temperature ductility. It has a proven track record in unpainted exterior automotive applications. ISO1043: PC+PBT-I.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Ductility,Solvent resistance,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 14 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，5 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.70 to 1.0 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 20 | kJ/m² | |
| 23℃ | 55 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| Impact strength of cantilever beam notch | |||
| -40℃ | 160 | J/m | ASTM D256 |
| -30℃ | 170 | J/m | ASTM D256 |
| 0℃ | 600 | J/m | ASTM D256 |
| 23℃ | 700 | J/m | ASTM D256 |
| -30℃ | 20 | kJ/m² | ISO 180-1A |
| 0℃ | 45 | kJ/m² | ISO 180-1A |
| 23℃ | 50 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 64 mm span | 110 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span | 90.0 | ℃ | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64 mm span | 90.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 125 | ℃ | ASTM D1525, ISO 306/B50 12 19 |
| A50 | 160 | ℃ | ISO 306/A50 |
| B120 | 127 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| MD：23~80℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| TD：23~80℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.18 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1 mm | 18 | kV/mm | |
| 3.2 mm in oil | 17 | kV/mm | |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | ||
| 60 Hz | 2.0E-3 | ||
| 1 MHz | 0.020 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 96.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2200 | MPa | ASTM D638 |
| — | 2150 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 56.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2/50 |
| fracture | 55.0 | MPa | ASTM D638 |
| fracture | 56.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 5.0 | % | ASTM D638 |
| yield | 5.0 | % | ISO 527-2/50 |
| fracture | 50 | % | ASTM D638 |
| fracture | 50 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 2050 | MPa | ASTM D790 |
| — | 2050 | MPa | ISO 178 |
| bending strength | |||
| — | 85.0 | MPa | ISO 178 |
| Yield, 50 mm span | 80.0 | MPa | ASTM D790 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 30.0 | mg | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40.0 to 60.0 | °C | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 240 to 265 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 60.0 to 80.0 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |