| About |
|---|
| XENOY CL100S has been specifically developed to obtain good low temperature impact strength, excellent UV stability and resistance to occasional solvent and gasoline contact. XENOY CL100S is particularly suited for unpainted exterior automotive body components.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Solvent resistance,low-temperature impact resistance,Gasoline resistance,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，5 kg | 20.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD | 0.70 to 1.0 | % | Internal Method |
| TD | 0.70 to 1.0 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.50 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 35 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/2C |
| -20℃ | 10 | kJ/m² | ISO 179/2C |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| 23℃ | 30 | kJ/m² | ISO 179/2C |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ISO 179/1eU | |
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 21 | kJ/m² | ISO 180-1A |
| 23℃ | 46 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 | ISO 180/1U | |
| 23℃ | 无断裂 | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 110 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 90.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 150 | ℃ | ISO 306/A50 |
| B50 | 125 | ℃ | ISO 306 |
| B120 | 127 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~80℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| TD：23~80℃ | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.18 | W/m/K | ISO 8302 |
| Relative temperature index | 75.0 | ℃ | UL 746 |
| Electrical performance | 75.0 | ℃ | UL 746 |
| Impact mechanical performance | 75.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | IEC 60243-1 | ||
| 1 mm | 18 | kV/mm | IEC 60243-1 |
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 1 MHz | 3.30 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | 45 | mm/min | ISO 3795 |
| Flame retardant level | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| Level L | 94 | ISO 2039-2 | |
| Ball hardness | |||
| H358/30 | 96.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 5.0 | % | ISO 527-2/50 |
| fracture | 75 | % | ISO 527-2/50 |
| Bending modulus | 2200 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 30.0 | mg | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40 to 60 | °C | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 240 to 265 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 |
| 7. 120*10*4 mm |
| 8. Short-Time |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |