| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| THERMAL | Nominal value | Unit | Test method |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 112 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 112 | ℃ | ISO 72-2/Af |
| Vicat Softening Temp | |||
| 137 | ℃ | ISO 306 | |
| 140 | ℃ | ISO 306/B120 | |
| Linear coefficient of thermal expansion | |||
| MD，-6℃~80℃ | 6.8E-5 | cm/cm/℃ | ISO 11359-2 |
| MD，23℃~80℃ | 6.8E-5 | cm/cm/℃ | ISO 11359-2 |
| TD，-6℃~80℃ | 9.6E-5 | cm/cm/℃ | ISO 11359-2 |
| TD，23℃~80℃ | 9.6E-5 | cm/cm/℃ | ISO 11359-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact performance of simply supported beams (23 ℃) | 6 | kJ/m2 | ISO 180/1A |
| Impact performance of cantilever beams | |||
| Gap, -6 ℃ | 6 | kJ/m2 | ISO 180/1A |
| Gap, 23 ℃ | 8 | kJ/m2 | ISO 180/1A |
| No gap, -6 ℃ | 80 | kJ/m2 | ISO 180/1U |
| No gap, 23 ℃ | 100 | kJ/m2 | ISO 180/1U |
| Instrument impact total energy, 23 ° C | 45 | N.m | ASTM D3763 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 366℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 365℃，5 kg | 0.610 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Equilibrium, 23 ℃ | 0.42 | % | ISO 62 |
| Saturation, 23 ℃, 50% RH | 0.14 | % | ISO 62 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.5 to 0.6 | % |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4399 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 56 | MPa | ISO 527-2/5 |
| fracture | 50 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 3.2 | % | ISO 527-2/5 |
| fracture | 8.0 | % | ISO 527-2/5 |
| Bending modulus | 4199 | MPa | ISO 178 |
| bending strength | 90 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| drying temperature | 110~120 | °C | |
| Drying time | 4~6 | hrs | |
| Maximum moisture content | 0.02 | % | |
| Melt Temperature | 260 – 280 | °C | |
| Hopper temperature | 60~80 | °C | |
| Front temperature | 260~280 | °C | |
| Mid section temperature | 250~257 | °C | |
| Post stage temperature | 240~270 | °C | |
| Nozzle temperature | 260~275 | °C | |
| Mold temperature | 60~100 | °C | |
| Forming temperature | 265~275 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |