| About |
|---|
| Xenoy* ENH2900 is a Non-Braominated, Non Chlorinated flame retarded PC/PBT resin with good flow, high impact and excellent chemical resistance. It was designed quite suitable for E&E housing applications&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,Halogen free,Flame Characteristics,Solvent resistance |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 266℃，5.0kg | 26 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.80 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2480 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 63.0 | MPa | |
| fracture | 42.0 | MPa | |
| Tensile strain | |||
| yield | 4.0 | % | |
| fracture | 65 | % | |
| Bending modulus | |||
| 50 mm span | 2240 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 89.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 550 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 65.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 102 | ℃ | ASTM D1525 6 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.10 mm | V-1 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VB |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 220 to 255 | °C | |
| Barrel middle temperature | 220 to 265 | °C | |
| Barrel front temperature | 245 to 275 | °C | |
| Nozzle temperature | 245 to 275 | °C | |
| Processing (melt) temperature | 245 to 275 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |