| About |
|---|
| Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, Gamma and Steam sterilizable.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Steam sterilized,Biocompatible,Hypocrystalline,Radiation disinfection,Solvent resistance,Ethylene oxide disinfection |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 1900 | MPa | ASTM D638 |
| Tensile modulus | 1900 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 35.0 | MPa | ASTM D638 |
| fracture | 37.0 | MPa | ISO 527-2/50 |
| yield | 43.0 | MPa | ASTM D638 |
| yield | 44.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 100 | % | ISO 527-2/50 |
| fracture | 150 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/50 |
| yield | 4.0 | % | ASTM D638 |
| Bending modulus | 1800 | MPa | ISO 178 |
| 50 mm span | 1900 | MPa | ASTM D790 |
| bending strength | 64.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 43.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 70 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -30℃ | No Break | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 750 | J/m | ASTM D256 |
| 23℃ | 800 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 20 | kJ/m² | ISO 180-1A |
| 23℃ | 65 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| -40℃ | No Break | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 100 | J | ASTM D3763 |
| Multi axial instrumented impact energy | 100 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 60.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa, unannealed, 3.2 mm | 60.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 95.0 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | 117 | ℃ | ASTM D1525 10 |
| Vicat Softening Temp | |||
| B50 | 117 | ℃ | ISO 306 |
| B120 | 120 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| TD：-40~40℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃ | 1.0E-4 | 1/℃ | ASTM E831 |
| MD | ISO 11359-2 | ||
| -40 to 40 ℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| 23 to 60 ℃ | 1.3E-4 | cm/cm/℃ | ISO 11359-2 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D792 |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，5 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.2 to 1.6 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.40 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.050 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 260℃，1500 sec^-1 | 210 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40 to 60 | °C | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 240 to 265 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |