| About |
|---|
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hrs | 0.14 | % | ASTM D570 |
| 23 ℃, equilibrium | 0.6 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.6 – 0.9 | % | Internal Method |
| TD：3.2 mm | 0.6 – 0.9 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 801 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 129 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 121 | ℃ | ASTM D648 |
| Relative temperature index | |||
| Elec | 75 | ℃ | UL 746B |
| Mech，w/ impact | 75 | ℃ | UL 746B |
| Mech，w/o impact | 75 | ℃ | UL 746B |
| Linear coefficient of thermal expansion | |||
| MD：-40℃ – 40℃ | 5.4E-05 | 1/℃ | ASTM E831 |
| TD：-40℃ – 40℃ | 6.12E-05 | 1/℃ | ASTM E831 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 55 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 120 | % | ASTM D638 |
| Bending modulus | |||
| 1.3 mm/min, 50.0 mm span | 2240 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 1.3 mm/min, 50.0 mm span | 86 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Temperature at the rear of the barrel | 250 to 270 | °C | |
| Temperature in the middle of the barrel | 255 to 275 | °C | |
| Front temperature of material barrel | 260 to 280 | °C | |
| Nozzle temperature | 255 to 275 | °C | |
| Processing (melt) temperature | 260 to 280 | °C | |
| Mold temperature | 65 to 95 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Exhaust hole depth | 0.013 to 0.020 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |