| About |
|---|
| X5500EX主要在薄膜挤出成型中得到广泛的应用。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good surface appearance,High liquidity,High Heat Resistance,Good tear strength |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 66 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, Type I, 50 mm/min | 63 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, Type I, 50 mm/min | 5.5 | % | ASTM D638 |
| Tensile strain | |||
| Fracture, Type I, 50 mm/min | 95 | % | ASTM D638 |
| Tensile modulus | |||
| 50 mm/min | 2452.50 | MPa | ASTM D638 |
| bending strength | |||
| Fracture, 1.30 mm/min, 50 mm span | 94.176 | MPa | ASTM D790 |
| Yield, 1.30 mm/min, 50 mm span | 97.119 | MPa | ASTM D790 |
| Bending modulus | |||
| 1.3mm/min，跨度50mm | 2275.92 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| 23℃ | 2156 | J/m | ASTM D4812 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 98.0 | J/m | ASTM D256 |
| Total energy of instrument impact | |||
| 23℃ | 713 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 132 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 108 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 123 | ℃ | ASTM D648 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.6-0.8 | % | Internal Method |
| MD：3.2 mm | 0.5-0.7 | % | Internal Method |
| Melt Flow Rate | |||
| 250℃，5.0kg | 6.5 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.04 | % | ISO 62 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Drying temperature | 120 | ℃ | |
| Drying time | 3-4 | hrs | |
| Drying time (cumulative) | 12 | hrs | |
| Maximum water content | 0.02 | % | |
| Melting temperature | 250-265 | ℃ | |
| Nozzle temperature | 245-260 | ℃ | |
| Front temperature | 250-265 | ℃ | |
| Mid section temperature | 245-260 | ℃ | |
| Post stage temperature | 240-255 | ℃ | |
| Mold temperature | 50-75 | ℃ | |
| Back pressure | 0.3-0.7 | MPa | |
| Screw speed | 50-100 | rpm | |
| Shooting cylinder size | 40-80 | % | |
| Depth of exhaust groove | 0.025-0.038 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |