XSTRAND™ GF30-PA6

About
Developed by Owens Corning, a world leader in composite solutions, XSTRAND™ GF30-PA6 filament for 3D printing is a reinforced material designed to be compatible with any standard Fused Filament Fabrication 3D printer (1.75 and 2.85 mm diameters available). Benefits Very high stiffness and strength (up to +250% compare ABS) Large operational temperature range (-20°C to 120°C) Good chemical and UV resistance High wear resistance Excellent layer adhesion Reduced warping effect compared to neat PA6 Potential Applications XSTRAND™ GF30-PA6 is designed for functional prototyping and demanding applications such as industrial tooling, transportation, electronics, small appliances, sports u0026amp; leisure…

About

Developed by Owens Corning, a world leader in composite solutions, XSTRAND™ GF30-PA6 filament for 3D printing is a reinforced material designed to be compatible with any standard Fused Filament Fabrication 3D printer (1.75 and 2.85 mm diameters available). Benefits Very high stiffness and strength (up to +250% compare ABS) Large operational temperature range (-20°C to 120°C) Good chemical and UV resistance High wear resistance Excellent layer adhesion Reduced warping effect compared to neat PA6 Potential Applications XSTRAND™ GF30-PA6 is designed for functional prototyping and demanding applications such as industrial tooling, transportation, electronics, small appliances, sports u0026amp; leisure…

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,High elastic,Antifreeze,Good bond,Good wear resistance,Heat Resistance, Good,Solvent resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.17	g/cm³	ISO 1183/A
Water absorption rate
Saturation, 23 ℃	9.6	%
Equilibrium, 23 ℃, 50% RH	0.58	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	7400	MPa	ISO 527-1-2
Tensile stress
yield	102	MPa
fracture	102	MPa
Tensile strain
fracture	2.1	%	ISO 527-2/1
Bending modulus	6100	MPa	ISO 178
bending strength
yield	170	MPa
fracture	166	MPa

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	124	℃	ISO 75-2/A
Melting temperature	206	℃	ISO 11357-3

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.