| About |
|---|
| XT polymer X800RG compound is an impact-modified acrylic-based multipolymer for molding and extrusion applications. Typical properties of XT® polymer acrylic-based multipolymer compounds are: outstanding thermoformability superior heat distortion temperatures excellent bonding and welding capabilities good impact strength good light transmission resistant to EtO, gamma and E-beam sterilization resistant to PVC stabilizers The special properties of XT polymer X800RG compound are: high melt flow rate good chemical resistance Application: Used for food packaging and appliance parts.&& |
| Product Description | |
|---|---|
| Supplier | ROHM |
| Generic | PMMA |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,High liquidity,E-beam disinfection,Food contact compliance,High Heat Resistance,Radiation disinfection,Solvent resistance,Welding,Ethylene oxide disinfection,Agglomerability |
| Availabilitys | North America,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ASTM D792 |
| Apparent density | 0.65 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 11 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Water absorption rate | |||
| balance | < 0.30 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 0℃，6.4mm | 64 | J/m | ASTM D256 |
| 23℃，6.4mm | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed, 6.35 mm | 85.6 | ℃ | ASTM D648 |
| Vicat Softening Temp | 93.9 | ℃ | ASTM D1525 |
| Linear coefficient of thermal expansion | |||
| MD：0~100℃ | 8.6E-5 | 1/℃ | ASTM D696 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3200 µm | 86.0 | % | ASTM D1003 |
| Haze | |||
| 3200 µm | 5.0 | % | ASTM D1003 |
| Yellowness index | |||
| 3.20 mm | -1.0 | YI | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2960 | MPa | ASTM D638 |
| tensile strength | 43.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 6.0 | % | ASTM D638 |
| yield | 4.0 | % | ASTM D638 |
| Bending modulus | 2210 | MPa | ASTM D790 |
| bending strength | 66.9 | MPa | ASTM D790 |
| Rockwell hardness | |||
| M-level | 22 | ASTM D785 |
| Notes |
|---|
| 1. 301 tint only |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |