| About |
|---|
| Product Description | |
|---|---|
| Supplier | ENEOS |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Low warping,Excellent Processability,Weather resistance is good,Solvent resistance,V-0,Flame Characteristics,Good Rigidity |
| Availabilitys | Asia Pacific,North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.86 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 48hr | 4.0E-3 | % | ASTM D570 |
| Ash Content | 49 | % | ASTM D5630 |
| Shrinkage rate | ASTM D955 | ||
| TD | 0.41 | % | ASTM D955 |
| MD | 0.058 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 15500 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 110 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.0 | % | ASTM D638 |
| Bending modulus | 16500 | MPa | ASTM D790 |
| bending strength | |||
| fracture | 168 | MPa | ASTM D790 |
| Fracture bending strain | 1.40 | % | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Complete fracture | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| Complete fracture | 19 | kJ/m² | ISO 179 |
| Notched impact strength of cantilever beam | |||
| Complete fracture | 25.2 | kJ/m² | ASTM D256 |
| Impact strength of cantilever beam notch | |||
| Complete fracture | 5.50 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 288 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 245 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：0~200℃ | 5.8E-5 | 1/℃ | ASTM E831 |
| TD：0~200℃ | 6.6E-4 | 1/℃ | ASTM E831 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.20 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 150 | °C | |
| Drying time | 6.0 to 8.0 | hr | |
| Processing (melt) temperature | 330 to 360 | °C | |
| Mold temperature | 70 to 160 | °C | |
| Locking force | 2.8 to 5.5 | kN/cm² | |
| Screw length to diameter ratio | 20.0 : 1.0 to 24.0 : 1.0 | ||
| Screw compression ratio | 2.5:1.0 to 3.0:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |