XYLEX™ X7200 resin

About
一般用途，紫外线稳定剂

Product Description
Supplier	SABIC
Generic	PC+PET
Material Status	Commercial: Active
Features	Weather resistance is good
Availabilitys	North America

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Shore hardness	75		ASTM D2240
tensile strength
Yield, 50 mm/min	55	MPa	ISO 527
Fracture, 50 mm/min	56	MPa	ISO 527
Tensile strain
屈服，5mm/min	5	%	ISO 527
Fracture, 50 mm/min	>150	%	ISO 527
Tensile modulus
1 mm/min	2000	MPa	ISO 527
bending strength
Yield, 2 mm/min	75	MPa	ISO 178
Bending modulus
2 mm/mim	2000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Total energy of instrument impact
23℃	97	J	ASTM D 3763
Impact strength of cantilever beam notch
23℃	910	J/m	ASTM D256
23℃，80104	8	kJ/m²	ISO 180-1A
80104 -30℃	5	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	115	℃	ASTM D1525
Hot deformation temperature
1.8 MPa, 100 mm span	99	℃	ISO 75/Ae
Unannealed, 3.2 mm
0.45 MPa	96	℃	ASTM D 648
1.8MPa	90	℃	ASTM D 648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	1.05E-04	1/℃	ASTM E 831
transverse	1.05E-04	1/℃	ASTM E 831
Thermal conductivity coefficient	0.23	W/m/℃	ISO 8302
Linear expansion coefficient, 23 ℃ to 60 ℃
flow	8.E-05	1/℃	ISO 11359-2
transverse	8.E-05	1/℃	ISO 11359-2
Vicat Softening Temp	115
Ball pressure test
Maximum approximation value	105	℃	IEC 60695-10-2

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.5 – 0.7	%	Internal Method
TD：3.2 mm	0.5 – 0.7	%	Internal Method
Melt Flow Rate
300℃，2.16kg	12	g/10min	ASTM D1238
Density	1.18		ISO 1183
Melt Volume Rate
300℃，2.16 kg	12	cm³/10min	ISO 1133

optical performance	Nominal value	Unit	Test method
Transmittance
2.54 mm	88	%	ASTM D1003
Haze
2.54 mm	1.1	%	ASTM D1003
Refractive index	1.557		ISO 489

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	>1.E+15	ohms·cm	ASTM D257
Surface resistivity	> 1.0E+15	ohms/sq	ASTM D257
Compared to the leakage tracing index	0	PLC Code	UL 746A

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
94V-2 flame level assessment	3	mm	UL 94
Glowing wire flammability index
750 ℃, through	1	mm	IEC 60695-2-12

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	80 – 95
Drying time	3 – 5	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.02	%
Melt temperature	250 – 270	°C
Nozzle temperature	250 – 270	°C
Front Section Zone 3 Temperature	250 – 270	°C
Temperature in Zone 2 of the middle section	245 – 265	°C
Temperature in Zone 1 of the rear section	240 – 250	°C
Mold temperature	45 – 60	°C
Back pressure	0.2 – 0.5	MPa
Screw speed	20 – 100	rpm
Shoot to cylinder size	40 – 80	%
Depth of exhaust groove	0.013 – 0.02	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.