XYLEX™ X8300CL resin

About
PC +聚酯，UV稳定，透明，

Product Description
Supplier	SABIC
Generic	PC+PET
Material Status	Commercial: Active
Features	Weather resistance is good,Good Clarity
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	55	MPa	ISO 527
Fracture, 50 mm/min	54	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	>5	%	ISO 527
Fracture, 50 mm/min	>200	%	ISO 527
Tensile modulus
1 mm/min	1600	MPa	ISO 527
bending strength
Fracture, 2 mm/min	78	MPa	ISO 178
Bending modulus
2 mm/mim	1700	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	1140	J/m	ASTM D256
-30℃	70	J/m	ASTM D256
Total energy of instrument impact
23℃	97	J	ASTM D 3763
Charpy Notched Impact Strength	10	kJ/m²	ISO 179-1eA
Impact strength of cantilever beam notch
23℃，80104	8	kJ/m²	ISO 180-1A
80104 -30℃	7	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	96	℃	ASTM D1525
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	1.05E-04	1/℃	ASTM E 831
transverse	1.05E-04	1/℃	ASTM E 831
Hot deformation temperature
1.8 MPa, 64 mm span	78	℃	ISO 75/Af
1.8 MPa, 100 mm span	80	℃	ISO 75/Ae
Unannealed, 3.2 mm
0.45 MPa	79	℃	ASTM D 648
1.8MPa	75	℃	ASTM D 648
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	9.E-05	1/℃	ISO 11359-2
transverse	9.E-05	1/℃	ISO 11359-2
Linear expansion coefficient, 23 ℃ to 60 ℃
flow	9.E-05	1/℃	ISO 11359-2
transverse	9.E-05	1/℃	ISO 11359-2
Vicat Softening Temp
B50	91	℃	ISO 306
B120	96	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Density	1.2		ASTM D792
Shrinkage rate
MD：3.2 mm	0.5 – 0.8	%	Internal Method
Melt Flow Rate
300℃，2.16kg	15	g/10min	ASTM D1238
Density	1.17	g/cm³	ISO 1183
Water absorption rate
Saturation, 23 ℃
（23℃/sat）	0.5	%	ISO 62
（23℃ / 50% RH）	0.2	%	ISO 62
Melt Volume Rate
265℃，2.16 kg	15	cm³/10min	ISO 1133

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	65 – 75
Drying time	3 – 5	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.02	%
Melt temperature	245 – 265	°C
Nozzle temperature	245 – 265	°C
Front Section Zone 3 Temperature	245 – 265	°C
Temperature in Zone 2 of the middle section	240 – 260	°C
Temperature in Zone 1 of the rear section	245 – 250	°C
Mold temperature	45 – 60	°C
Back pressure	0.2 – 0.5	MPa
Screw speed	20 – 100	rpm
Shoot to cylinder size	40 – 80	%
Depth of exhaust groove	0.013 – 0.02	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.