| About |
|---|
| 40% Glass Reinforced, Enhanced Mechanical Strength&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Europe,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding shrinkage | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 11 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 57 | kJ/m² | ISO 179/1eU |
| 23℃ | 56 | kJ/m² | ISO 179/1eU |
| Izod Notched Impact strength | |||
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| Izod Unnotched Impact strength of cantilever beam | |||
| 23℃ | 48 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.8 MPa, unannealed | 260 | ℃ | ISO 75-2/A |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Coeff. of linear thermal expansion | ISO 11359-2 | ||
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.5E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 8.5E-5 | 1/℃ | ISO 11359-2 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | kV/mm | IEC 60243-1 |
| Compared Tracking Index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 0.8 mm | V-0 | ||
| 1.50 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 100 | ISO 2039-2 | |
| R-level | 121 | ISO 2039-2 | |
| Tensile Modulus | ISO 527-2 | ||
| — | 15000 | MPa | ISO 527-2 |
| 120℃ | 7300 | MPa | ISO 527-2 |
| 160℃ | 5200 | MPa | ISO 527-2 |
| 200℃ | 3400 | MPa | ISO 527-2 |
| Tensile Strength | ISO 527-2 | ||
| Broken BRK | 200 | MPa | ISO 527-2 |
| Broken BRK, 120 ℃ | 105 | MPa | ISO 527-2 |
| Broken BRK, 160 ℃ | 73.0 | MPa | ISO 527-2 |
| Broken BRK, 200 ℃ | 55.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Broken BRK | 2.0 | % | ISO 527-2 |
| Broken BRK, 120 ℃ | 3.1 | % | ISO 527-2 |
| Broken BRK, 160 ℃ | 3.9 | % | ISO 527-2 |
| Broken BRK, 200 ℃ | 6.4 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | ||
| — | 14500 | MPa | ISO 178 |
| 120℃ | 10000 | MPa | ISO 178 |
| 160℃ | 5000 | MPa | ISO 178 |
| 200℃ | 4200 | MPa | ISO 178 |
| Flexural Strength | 300 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 130-140 | °C | |
| Drying Time | 2-6 | hr | |
| Rear Temperature Zone 1 | 300-320 | °C | |
| Middle Temperature Zone 2 | 310-330 | °C | |
| Front Temperature Zone 3 | 320-340 | °C | |
| Nozzle temperature | 310-340 | °C | |
| Melt Temperature | 310-340 | °C | |
| Mold Temperature | 140-150 | °C | |
| Back Pressure | 3.0-10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |