| About |
|---|
| 65% Glass/Mineral Reinforced&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PPS |
| Material Status | Commercial: Negative |
| Features | V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.97 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.40 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.020 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.3 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 27 | kJ/m² | ISO 179/1eU |
| 23℃ | 25 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 260 | ℃ | ISO 75-2/A |
| Melting temperature | 280 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 2.4E-5 | 1/℃ | ISO 11359-2 |
| TD | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 225 | V | IEC 60112 |
| Flammability level | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.70 mm | V-0 | ||
| Flame retardant level | |||
| 1.50 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 101 | ISO 2039-2 | |
| R-level | 120 | ISO 2039-2 | |
| Tensile modulus | ISO 527-2 | ||
| — | 21000 | MPa | ISO 527-2 |
| 120℃ | 11400 | MPa | ISO 527-2 |
| 160℃ | 8500 | MPa | ISO 527-2 |
| 200℃ | 5500 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 150 | MPa | ISO 527-2 |
| Fracture, 120 ℃ | 98.0 | MPa | ISO 527-2 |
| Fracture, 160 ℃ | 70.0 | MPa | ISO 527-2 |
| Fracture, 200 ℃ | 58.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 1.0 | % | ISO 527-2 |
| Fracture, 120 ℃ | 1.6 | % | ISO 527-2 |
| Fracture, 160 ℃ | 2.2 | % | ISO 527-2 |
| Fracture, 200 ℃ | 3.8 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| — | 20000 | MPa | ISO 178 |
| 120℃ | 14000 | MPa | ISO 178 |
| 160℃ | 9100 | MPa | ISO 178 |
| 200℃ | 7000 | MPa | ISO 178 |
| bending strength | 230 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 310 to 330 | °C | |
| Barrel front temperature | 320 to 340 | °C | |
| Nozzle temperature | 310 to 340 | °C | |
| Processing (melt) temperature | 310 to 340 | °C | |
| Mold temperature | 140 to 150 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |