| About |
|---|
| 70% Glass/Mineral Reinforced&& |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PPS |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.00 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.30 | % | |
| MD | 0.20 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 26 | kJ/m² | |
| 23℃ | 22 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 280 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 265 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 185 | ℃ | ISO 75-2/C |
| Linear coefficient of thermal expansion | |||
| MD | 1.5E-5 | 1/℃ | |
| MD | 1.8E-5 | 1/℃ | |
| TD | 2.0E-5 | 1/℃ | |
| TD | 5.0E-5 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | V-0 | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 101 | ||
| R-level | 120 | ||
| Tensile modulus | |||
| — | 22000 | MPa | |
| 120℃ | 13000 | MPa | |
| 160℃ | 9100 | MPa | |
| 200℃ | 7600 | MPa | |
| tensile strength | |||
| fracture | 150 | MPa | |
| Fracture, 120 ℃ | 90.0 | MPa | |
| Fracture, 160 ℃ | 65.0 | MPa | |
| Fracture, 200 ℃ | 55.0 | MPa | |
| Tensile strain | |||
| fracture | 0.90 | % | |
| Fracture, 120 ℃ | 1.7 | % | |
| Fracture, 160 ℃ | 1.9 | % | |
| Fracture, 200 ℃ | 2.0 | % | |
| Bending modulus | |||
| — | 21000 | MPa | |
| 120℃ | 12000 | MPa | |
| 160℃ | 8000 | MPa | |
| 200℃ | 6800 | MPa | |
| bending strength | 230 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 130 to 140 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 310 to 330 | °C | |
| Barrel front temperature | 320 to 340 | °C | |
| Nozzle temperature | 310 to 340 | °C | |
| Processing (melt) temperature | 310 to 340 | °C | |
| Mold temperature | 140 to 150 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 3.00 to 10.0 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. above Tg |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |